ASTM B473 Sheets & Plates, ASME SB473 Sheets, Alloy 20 Plates Supplier, Manufacturer and Exporter in India
Din 2.4660 Alloy 20 Sheets , UNS N08020 Plates, Alloy 20 Sheets & Plates, Alloy 20 Nuts Suppliers in India.
ALLOY 20 SHEETS AND PLATES GENERAL PROPERTIES:
Alloy 20 (UNS N08020) is an austenitic, nickel-iron-chromium based super alloy with additions of Copper and Molybdenum which provide resistance to hostile environments, pitting, and crevice corrosion. It is also stabilized with Columbium to minimize carbide precipitation during welding. Alloy 20 appears to fall between both the stainless and nickel categories as it contains characteristics of both. It was designed for maximum resistance to acid attack and demonstrates superior resistance to stress-corrosion cracking in boiling 20% to 40% sulfuric acid, and also has excellent general corrosion resistance to sulfuric acid and to chloride stress corrosion cracking. Alloy 20 has good mechanical properties at both ambient and elevated temperatures, up to approximately
930°F (500°C) and is readily fabricated by usual industrial processes.
ALLOY 20 SHEETS AND PLATES APPLICATIONS:
Alloy 20 was originally designed for use in sulfuric acid related applications; however, it is now frequently used in a wide variety of industries. Applications that commonly use Alloy 20 include:
Chemical and allied industries
Food and dye production
Heat exchangers
Explosives
Tanks
Valves
Pickling racks
Manufacture of synthetic rubber and plastics
Pharmaceuticals
SO2 scrubbers and other severe environments
ALLOY 20 SHEETS AND PLATES CORROSION RESISTANCE:
Excellent resistance to general corrosion, pitting, and crevice corrosion in chemicals containing chlorides and sulfuric, phosphoric, and nitric acids.
Nickel content aids in chloride ion stress and corrosion resistance.
Additions of Copper and Molybdenum provide resistance to hostile environments, pitting, and crevice corrosion.
Chromium adds to its resistance of oxidizing environments such as nitric acids.
Columbium reduces the effects of carbide precipitation.
ALLOY 20 SHEETS AND PLATES WELDABILITY:
All commonly used welding methods, with the exception of oxyacetylene, can be successfully used.
The presence of Columbium tends to minimize the precipitation of carbides in the heat-affected zone, so the material may be used in the as-welded condition in most cases.
Pre-heating is not required.
ALLOY 20 SHEETS AND PLATES HEAT TREAMENT:
Cannot be hardened by heat treatment.
Stabilized-annealing is done at 1750-1850°F, followed by water quenching.
Stress relieving can be performed on annealed material up to 950°F.
ALLOY 20 SHEETS AND PLATES PROCESSING - HOT FORMING:
Heat uniformly to a starting temperature of 2100-2225°F. Finish forging before the stock drops below 1800°F.
In order to stabilize the material after hot working operations, reheat at 1750-1850°F for a minimum of 1/2-hour per one inch of thickness and water quench.
ALLOY 20 SHEETS AND PLATES PROCESSING - COLD FORMING:
Alloy 20 has good cold formability. Bending, drawing and pressing, and other forming operations that occur in the production of fabricated items are readily performed.
Alloy 20 can normally be press brake bent over a radius twice the materials thickness.
After cold reductions of more than 15%, a final stabilizing annealing is often required.
ALLOY 20 SHEETS AND PLATES MACHINABILITY:
Because of Alloy 20′s high work-hardening rate the following are required:
Only low surface-cutting speeds are possible compared with low-alloy standard austenitic stainless steel.
Tools should be engaged at all times.
Heavy feeds are important in getting below the work-hardened 'skin'.
ALLOY 20 SHEETS AND PLATES CHEMICAL PROPERTIES:
TYPE
C
Cr
Cu
Fe
Mn
Mo
Ni
P
Si
S
Nb
(Cb)
Alloy 20
UNS
N08020
0.07
max
min: 19.00
max: 21.00
min: 3.00
max: 4.00
Balance
2.00
max
min: 2.00
max: 3.00
min: 32.00
max: 38.00
0.045
max
1.00
max
0.035
max
8 XC min
1.00 max
ALLOY 20 SHEETS AND PLATES MECHANICAL PROPERTIES:
Stabilized-Annealed Condition
Product Form
Tensile
Strength, ksi (min)
Yield
Strength, 0.2% offset ksi (min)
Elongation % (min)
Reduction of Area
% (min)
Hardness
Brinell (max)
Hardness
Rockwell B (max)
Plate, Sheet
80
35
30
—
217
95
Bar
80
35
30
50
—
—
ALLOY 20 SHEETS AND PLATES PHYSICAL PROPERTIES:
Density
Specific Gravity
Specific Heat
at 32 to 212°F
Electrical Resistivity
at 68°F
Poissons Ratio
Magnetic Permeability
at 68°F
Modulus of Elasticity
at 68°F
0.292 lbs/in3
8.08
0.12 BTU/lb/°F
644 ohm-cir mil/ft
0.31
1.002 Mu
29.3 x 106 psi
ALLOY 20 SHEETS AND PLATES ,GRADES WITH THICKNESS AND WIDTH
We export our ALLOY 20 SHEETS AND PLATES products to Western and Eastern Europe, Saudi Arabia, Bangladesh, United States, United Arab Emirates, Canada, Angola, Argentina, Austria, Azerbaijan, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia etc. We are sure that we also can cover the requirements requested by your company you can email us at