STAINLESS STEEL 430 SHEETS AND PLATES GENERAL PROPERTIES:

Grade 430 is a ferritic, straight chromium, non-hardenable grade, combining good corrosion resistance and formability characteristics with useful mechanical properties. Its ability to resist nitric acid attack permits its use in specific chemical applications but automotive trim and appliance components represents its largest fields of application.

Grade 430F is the free-machining version of this grade, available in bar form for use in automatic screw machines. Grade 434 is the molybdenum bearing version of Grade 430 and has the same useful combination of properties. Its molybdenum addition improves corrosion resistance.

These properties for 430 are specified for flat rolled product (plate, sheet and coil) in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as forgings and bar in their respective specifications. Properties of Grade 430F are specified for bar in ASTM A582.

STAINLESS STEEL 430 SHEETS AND PLATES APPLICATIONS:

Typical applications for 430 grade include:

• Linings for dish washers
• Refrigerator cabinet panels
• Automotive trim
• Lashing Wire
• Element Supports
• Stove trim rings
• Fasteners
• Chimney Liners

Typical applications for 430F grade include:

• Repetition machined components

STAINLESS STEEL 430 SHEETS AND PLATES CORROSION RESISTANCE:-

Grade 430 has good resistance to a wide variety of corrosive enviornments, including nitric acid and some organic acids. It attains its maximum corrosion resistance when in the highly polished or buffed condition. In general its resistance to pitting and crevice corrosion resistance is close to that of grade 304. Stress corrosion cracking resistance of Grade 430 is very high, as it is for all ferritic grades.

Like other high-sulphur free machining grades 430F has much reduced resistance to pitting and crevice corrosion compared to its non-free machining equivalent.

STAINLESS STEEL 430 SHEETS AND PLATES HEAT TREATMENT:

• Solution Annealing – Heat to 815-845°C, hold for ½ hour per 25mm of thickness, slow furnace cool to 600°C and then quickly air cool. Slow cooling from 540-400°C will cause embrittlement.
• Sub-Critical anneal – Heat to 760-815°C and then air cool or water quench.
• This grade is not hardenable by thermal treatment.

STAINLESS STEEL 430 SHEETS AND PLATES WELDING:

• Pre-heat at 150-200°C if welding is necessary.
• Embrittlement in the weld metal and heat affected zone can be relieved by a post-weld anneal at 790-815°C
• Grain refinement will not occur.

STAINLESS STEEL 430 SHEETS AND PLATES MACHINING:

• Easier to machine than the standard austenitic grades such as 304.
• Still a tendency for galling and pick-up on the cutting tool.
• Bars that have been lightly drawn are easier to machine than those in the annealed condition.
• Grade 430F, the free machining version of 430, is very much easier to machine.

STAINLESS STEEL 430 SHEETS AND PLATES FABRICATION:

• Lower work hardening rate makes bending and forming somewhat easier than for grade 304
• Lower ductility restricts very severe operations.
• Severe bends should be made with the bend axis at right angles to the rolling direction.
• Severe cold heading of 430 wire is possible.

STAINLESS STEEL 430 SHEETS AND PLATES COMPOSITION:

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	N
430	min. max.	- 0.12	- 1.00	- 1.00	- 0.040	- 0.030	16.0 18.0	-	- 0.75	-
430F	min. max.	- 0.12	- 1.25	- 1.00	- 0.06	0.15 -	16.0 18.0	-	-	-

STAINLESS STEEL 430 SHEETS AND PLATES MECHANICAL PROPERTIES:

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
430	450	205	22	89	183
430F	552 typical	379 typical	25 typical	-	262

STAINLESS STEEL 430 SHEETS AND PLATES PHYSICAL PROPERTIES:

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Coefficient of Thermal Expansion (mm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100°C (J/kg.K)	Electrical Resistivity (nW.m)
			0-100°C	0-315°C	0-538°C	at 100°C	at 500°C
430	7750	200	10.4	11.0	11.4	23.9	26.0	460	600
430F	7750	200	10.4	11.0	11.4	26.1	26.3	460	600

STAINLESS STEEL 430 SHEETS AND PLATES POSSIBLE ALTERNATIVE GRADES:

In the table below are a list of possible alternative grades to Grade 430.

Grade	Reason it  may be chosen instead of 430
430F	Higher machinability than 430 is needed in bar product, and reduced corrosion resistance is acceptable.
434	Better pitting resistance is required
304	Slightly higher corrosion resistance is needed, together with greatly improved ability to be welded and cold formed
316	Much better corrosion resistance is needed, together with greatly improved ability to be welded and cold formed
3CR12	A lower corrosion resistance is acceptable in a cost-critical application

STAINLESS STEEL PLATES,GRADES WITH THICKNESS AND WIDTH
Thickness Range of Stainless Plate	3/16″ Thru 6″ Thick Stainless Steel Plate
Common Widths of Stainless Plate Coil	48″ Wide – 60″ Wide – 72″ Wide – 78.75″ (2 Meter) wide – 84″ wide – 96″ wide – 120″ wide & other widths upon customer request.
200-300 Series Stainless Steel Grades	202- 301 – 304 – 304L – 304L Polished – 304H – 309 – 309S – 309H – 310 – 310S – 310H – 316L – 316L Polished – 317L – 317LMN – 321 – 321H – 330 – 347 347H
400 Series Stainless Steel Grades	405 – 410 – 410S – 416 – 420 – 440C
Duplex Stainless Steel Grades	LDX 2101 – Duplex 2205 – Duplex 2507
Precipitation Hardening Grades	17-4PH – 17-4 H1150 (per customer request) – 15-5PH
Nickel Alloy Grades	Alloy 20 – Alloy 200 – Alloy 400 – Alloy 600 – Alloy 800 – Alloy 800HT – Alloy C-276 (nickel grades may require lead time)

---