UNS S20200 Flat Bars, SS 202 Flat Bars, AISI SS 202 Stainless Steel 202 Flat Bars Supplier, Manufacturer and Exporter in India
Din 1.4373 SS 202 Flat Bars, SS UNS S20200 Flat Bars, Stainless Steel 202 Flat Rods, 202 Stainless Steel 202 Flat Bars Suppliers in India.
STAINLESS STEEL 202 FLAT BAR DESCRIPTION:
Type 202 Stainless Steel is an austenitic chromium-nickel-manganese stainless steel which was developed to conserve nickel. Type 202 is a lower cost alternative to conventional Cr-Ni stainless steels such as 301 and 304. Nickel is replaced by additions of manganese and nitrogen. It is non-hardenable by thermal treatment, but may be cold worked to high tensile strengths. Type 201 is essentially nonmagnetic in the annealed condition and becomes magnetic when cold worked. Type 201 can be substituted for Type 301 in many applications
STAINLESS STEEL 202 FLAT BAR PRODUCT FORMS:
Sheet, Strip
STAINLESS STEEL 202 FLAT BAR TYPICAL APPLICATIONS:
Typical applications for Types 202 are cookware, hose clamps, piston rings, transit car structural member, transit car roofing/siding, thermal window spacers, air bag containers, and truck trailer posts and door frames.
STAINLESS STEEL 202 FLAT BAR PROCESSING:
The annealing temperature for Type 202 is between 1850-2000°F. Rapid cooling through the carbide precipitation range (1500 – 800 ° F) is necessary to keep the carbides in solution and prevent sensitization. Type 201 is not hardenable by thermal treatment; it is only hardenable by cold working.
STAINLESS STEEL 202 FLAT BAR FORMING:
Type 202 has similar bending, forming and drawing characteristics to Type 301 stainless steel
STAINLESS STEEL 202 FLAT BAR WELDING:
Type 202 can be welded by all conventional methods applied to 18 percent chromium, 8 percent nickel steels. Filler metal of the conventional chromium-nickel analyses can be used. Like other austenitic stainless steels where carbon is not controlled below 0.03%, Type 202 is susceptible to intergranular corrosion in the weld heat affected zone.
STAINLESS STEEL 202 FLAT BAR CORROSION:
Type 202 is resistant to a wide variety of mild to moderately corrosive environments. It has corrosion resistance approaching that of Types 301and has been successfully substituted for 304 in many mild environments.
STAINLESS STEEL 202 FLAT BAR CHEMICAL PROPERTIES:
| Element | Type 201 |
|---|---|
| Carbon | 0.15x |
| Manganese | 5.5 - 7.5 |
| Sulfur | 0.03X |
| Phosphorus | 0.060x |
| Silicon | 1.0 x |
| Chromium | 16 - 18 |
| Nickel | 3.5 -5.5 |
| Nitrogen | 0.25x |
STAINLESS STEEL 202 FLAT BAR MECHANICAL PROPERTIES:
| Type | Yield Strength 0.2% offset (KSI) | Tensile Strength (KSI) | % Elongation (2" Gauge length) |
Hardness Rockwell |
|---|---|---|---|---|
| 201 Ann | 38 min. | 75 min. | 40% min. | HRB 95 max. |
| 201 ¼ Hard | 75 min. | 125 min. | 25.0 min. | 25 – 32 HRC (typical) |
| 201 ½ Hard | 110 min. | 150 min. | 18.0 min. | 32 - 37 HRC (typical) |
| 201 ¾ Hard | 135 min. | 175 min. | 12.0 min. | 37 – 41 HRC (typical) |
| 201 Full Hard | 145 min. | 185 min. | 9.0 min. | 41 – 46 HRC (typical) |
STAINLESS STEEL 202 FLAT BAR PHYSICAL PROPERTIES:
| Density (lb./ in^2) @ RT | 0.283 | |
|---|---|---|
| Modulus of Elasticity in Tension (psi x 10^6) | 28.6 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 °F | 0.12 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212°F | 9.4 |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F) | 32 to 212°F | 8.7 |
| 32 to 600°F | 9.7 | |
| 32 to 1,000°F | 10.2 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 69 |
| Melting Point Range (oF) | 2550/2650 | |
| Oxidation Resistance - Continuous Service(oF) | 1550 | |
| Oxidation Resistance - Intermittent Service(oF) | 1500 |
- Width:25mm to 60mm
- Thickness:5mm to 12mm
- Finish :Hot Rolled Annealed & Pickled (HRAP)
- Length:3 to 6 Meters / 12 to 20 feet
- End Finish :Both ends are marked with special colors.
- Size tolerance:A276/484 / DIN 1028 (Full specification mentioned below)
- Packing:Bars are packed in 1000 to 1,200 kgs bundles in waterproof HDPE cloths, Standard Export Seaworthy, Marking of Sizes, Grade, Net Wt, Gross Wt, No of pieces, POD, Origin should Mentioned on Each bundles
- Marking:Size, Grade, Manufacture name on Each Bars/Pieces
- Delivery:60-75 Days from the order finalization
- Marking:Size, Grade, Manufacture name on Each Bars/Pieces
- Grades:AISI 304 / 304L, 201, 202, 316
We export our STAINLESS STEEL 202 FLAT BARS products to Western and Eastern Europe, Saudi Arabia, Bangladesh, United States, United Arab Emirates, Canada, Angola, Argentina, Austria, Azerbaijan, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia etc. We are sure that we also can cover the requirements requested by your company you can email us at harshsteel@ymail.com for your instant requirements.