STAINLESS STEEL 316 ANGLE GENERAL PROPERTIES:

Alloy 316/316L is molybdenum-bearing austenitic stainless steel. The higher nickel and molybdenum content in this grade allows it to demonstrate better overall corrosion resistant properties than 304, especially with regard to pitting and crevice corrosion in chloride environments. In addition, Alloy 316/ 316L provides excellent elevated temperature tensile, creep and stress-rupture strengths, as well as outstanding formability and weldability. 316L is the lower carbon version of 316 and is immune from sensitization; therefore, it is very frequently used in heavy gauge welded components.

STAINLESS STEEL 316 ANGLE APPLICATIONS:

• Food preparation equipment, especially in chloride environments
• Chemical processing, equipment
• Laboratory benches and equipment
• Rubber, plastics, pulp & paper machinery
• Pollution control equipment
• Boat fittings, value and pump trim
• Heat exchangers
• Pharmaceutical and textile industries
• Condensers, evaporators and tanks

STAINLESS STEEL 316 ANGLE CORROSION RESISTANCE:

• Generally more resistant than 304 in range of atmospheric environments and many corrosive media due to the increased chromium
  and molybdenum content.
• Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 122°F (50°C).
• Considered resistant to potable water with up to about 1000mg/L chlorides at ambient temperatures, reducing to about 500mg/L at
  140°F (60°C).
• Usually regarded as the "marine grade stainless steel" – but is not resistant to warm sea water.

STAINLESS STEEL 316 ANGLE HEAT RESISTANCE:

• Good oxidation resistance in intermittent service to 1600°F (870°C) and in continuous service to 1700°F (925°C)
• Grade 316L is more resistant to carbide precipitation.

STAINLESS STEEL 316 ANGLE WELDING CHARACTERISTICS:

• Excellent weldability by all standard fusion methods, both with and without filler metals.
• Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance, this is not required for grade 316L.

STAINLESS STEEL 316 ANGLE HEAT TREATMENT:

• Annealing temperature range is 1900 to 2100°F (1038 to 1149°C).
• Cannot be hardened by heat treatment.
• Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion.

STAINLESS STEEL 316 ANGLE PROCESSING - HOT FORMING:

• Most producers recommend a maximum forging temperature between 2100°F and 2300°F
• Do not forge below 1700°F (927°C) Best
• Corrosion resistance is obtained if the forgings are given a final anneal.

STAINLESS STEEL 316 ANGLE PROCESSING - COLD FORMING:

• 316/316L types being extremely tough and ductile, can be readily cold worked such as roll form, swaging, cold heading, deep drawing,
  bent, etc., without difficulty
• Severely cold formed parts should be annealed to remove stresses.

STAINLESS STEEL 316 ANGLE MACHINEABILITY:

• Type 316/316L is somewhat more difficult to machine than Type 304 because of its toughness.
• 316/316L machines with chip characteristics that are tough and strong.
• Chip breakers and curlers are advised.
• As large a tool as possible and great amounts of cutting fluid should be used.
• Heavy positive feeds at low speeds should be considered since 316/316L work hardens rapidly.

STAINLESS STEEL 316 ANGLE CHEMICAL PROPERTIES:

	C	Mn	Si	P	S	Cr	Mo	Ni	N
316 (S31600)	0.08 max	2.0 max	0.75 max	0.045 max	0.03 max	min: 16.0 max: 18.0	min: 2.0 max: 3.0	min: 10.0 max: 14.0	0.10 max
316L (S31603)	0.03 max	2.0 max	0.75 max	0.045 max	0.03 max	min: 16.0 max: 18.0	min: 2.0 max: 3.0	min: 10.0 max: 14.0	0.10 max

STAINLESS STEEL 316 ANGLE MECHANICAL PROPERTIES:

Grade	Tensile Strength ksi (min)	Yield Strength 0.2% ksi (min)	Elongation %	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
316 (S31600)	75	30	40	217	95
316L (S31603)	70	25	40	217	95

STAINLESS STEEL 316 ANGLE PHYSICAL PROPERTIES:

Density lbm/in3	Thermal Conductivity (BTU/h ft. °F)	Electrical Resistivity (in x 10-6)	Modulus of Elasticity (psi x 106	Coefficient of Thermal Expansion (in/in)/°F x 10-6	Specific Heat (BTU/lb/°F)	Melting Range (°F)
0.29 at 68°F	100.8 at 68 212°F	29.1 at 68°F	29	8.9 at 32 – 212°F	0.108 at 68°F	2500 to 2550
				9.7 at 32 – 1000°F	0.116 at 200°F
				11.1 at 32 – 1500°F

WHY TO CHOOSE HARSH STEEL STAINLESS STEEL ANGLE BARS?

• Corrosion resistance
• Durable
• Very sturdy
• Easy to install
• Fire and heat resistance
• Rust free
• Abrasion free

HARSH STEEL STAINLESS STEEL ANGLE BARS USED IN?

• Architectural applications
• Bridges
• Transmission towers
• Hoisting and conveying machinery
• Ships
• Industrial furnace
• Reaction tower
• Container frame and warehouse shelves
• Multi-storied building
• Fabrication

STAINLESS STEEL 316 ANGLE DETAILS:

• Finish:Hot Rolled Annealed & Pickled (HRAP)
• Length: 3 to 7 Meters / 12 to 24 feet
• End Finish: Both ends are marked with special colors
• Size tolerance : ASTM A276/484 / DIN 1028
• Packing: Bars are packed in 500 to 1,000 kgs bundles in waterproof HDPE cloth Standard Export Seaworthy.
• Delivery: Within 60-70 Days from the order finalization
• Grades : AISI 201, 202, 204cu, 304, 304L, 316, 410, 420, 430

STAINLESS STEEL 316 ANGLE SIZES:

Width (mm)	Thickness (mm)	Width (Inches)	Thickness (Inches)
20 x 20	3 to 5	3/4"	1/8 to 1/4
25 x 25	3 to 5	1"	1/8 to 1/4
30 x 30	3 to 5	1.1/8	1/8 to 1/4
32 x 32	3 to 6	1.1/4	1/8 to 1/4
35 x 35	3 to 6	1.3/8	1/8 to 1/4
38 x 38	3 to 6	1.1/2	1/8 to 1/4
40 x 40	3 to 6	1.5/8	1/8 to 1/4
45 x 45	3 to 6	1.3/4	1/8 to 1/4
50 x 50	3 to 6	2"	1/8 to 1/4
60 x 60	5 to 6	2.3/8	3/16 to 1/4
65 x 65	5 to 6	2.1/2	3/16 to 1/4
70 x 70	5 to 6	2.3/4	3/16 to 1/4
75 x 75	5 to 6	3"	3/16 to 1/4

---