UNS S43000 Angle, SS 430 Angles, Stainless Steel 430 Angles Supplier, Manufacturer and Exporter in India
Din 1.4016 SS 430 Angles, SS UNS S43000 Angles, Stainless Steel 430 Angles, 440 Stainless Steel Angles Suppliers in India.
STAINLESS STEEL 430 ANGLE GENERAL PROPERTIES:
Grade 430 is a ferritic, straight chromium, non-hardenable grade, combining good corrosion resistance and formability characteristics with useful mechanical properties. Its ability to resist nitric acid attack permits its use in specific chemical applications but automotive trim and appliance components represents its largest fields of application.
Grade 430F is the free-machining version of this grade, available in bar form for use in automatic screw machines. Grade 434 is the molybdenum bearing version of Grade 430 and has the same useful combination of properties. Its molybdenum addition improves corrosion resistance.
These properties for 430 are specified for flat rolled product (plate, sheet and coil) in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as forgings and bar in their respective specifications. Properties of Grade 430F are specified for bar in ASTM A582.
STAINLESS STEEL 430 ANGLE APPLICATIONS:
Typical applications for 430 grade include:
Linings for dish washers
Refrigerator cabinet panels
Automotive trim
Lashing Wire
Element Supports
Stove trim rings
Fasteners
Chimney Liners
Typical applications for 430F grade include:
Repetition machined components
STAINLESS STEEL 430 ANGLE CORROSION RESISTANCE:
Grade 430 has good resistance to a wide variety of corrosive enviornments, including nitric acid and some organic acids. It attains its maximum corrosion resistance when in the highly polished or buffed condition. In general its resistance to pitting and crevice corrosion resistance is close to that of grade 304. Stress corrosion cracking resistance of Grade 430 is very high, as it is for all ferritic grades.
Like other high-sulphur free machining grades 430F has much reduced resistance to pitting and crevice corrosion compared to its non-free machining equivalent.
STAINLESS STEEL 430 ANGLE HEAT TREATMENT:
Solution Annealing – Heat to 815-845°C, hold for ½ hour per 25mm of thickness, slow furnace cool to 600°C and then quickly air cool. Slow cooling from 540-400°C will cause embrittlement.
Sub-Critical anneal – Heat to 760-815°C and then air cool or water quench.
This grade is not hardenable by thermal treatment.
STAINLESS STEEL 430 ANGLE WELDING:
Pre-heat at 150-200°C if welding is necessary.
Embrittlement in the weld metal and heat affected zone can be relieved by a post-weld anneal at 790-815°C
Grain refinement will not occur.
STAINLESS STEEL 430 ANGLE MACHINING:
Easier to machine than the standard austenitic grades such as 304.
Still a tendency for galling and pick-up on the cutting tool.
Bars that have been lightly drawn are easier to machine than those in the annealed condition.
Grade 430F, the free machining version of 430, is very much easier to machine.
STAINLESS STEEL 430 ANGLE FABRICATION:
Lower work hardening rate makes bending and forming somewhat easier than for grade 304
Lower ductility restricts very severe operations.
Severe bends should be made with the bend axis at right angles to the rolling direction.
Severe cold heading of 430 wire is possible.
STAINLESS STEEL 430 ANGLE COMPOSITION:
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
430
min.
max.
-
0.12
-
1.00
-
1.00
-
0.040
-
0.030
16.0
18.0
-
-
0.75
-
430F
min.
max.
-
0.12
-
1.25
-
1.00
-
0.06
0.15-
16.0
18.0
-
-
-
STAINLESS STEEL 430 ANGLE vMECHANICAL PROPERTIES:
Grade
Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B) max
Brinell (HB) max
430
450
205
22
89
183
430F
552 typical
379 typical
25 typical
-
262
STAINLESS STEEL 430 ANGLE PHYSICAL PROPERTIES:
Grade
Density (kg/m3)
Elastic Modulus (GPa)
Mean Coefficient of Thermal Expansion
(mm/m/°C)
Thermal Conductivity
(W/m.K)
Specific Heat 0-100°C (J/kg.K)
Electrical Resistivity (nW.m)
0-100°C
0-315°C
0-538°C
at 100°C
at 500°C
430
7750
200
10.4
11.0
11.4
23.9
26.0
460
600
430F
7750
200
10.4
11.0
11.4
26.1
26.3
460
600
STAINLESS STEEL 430 ANGLE POSSIBLE ALTERNATIVE GRADES:
In the table below are a list of possible alternative grades to Grade 430.
Grade
Reason it may be chosen instead of 430
430F
Higher machinability than 430 is needed in bar product, and reduced corrosion resistance is acceptable.
434
Better pitting resistance is required
304
Slightly higher corrosion resistance is needed, together with greatly improved ability to be welded and cold formed
316
Much better corrosion resistance is needed, together with greatly improved ability to be welded and cold formed
3CR12
A lower corrosion resistance is acceptable in a cost-critical application
We export our STAINLESS STEEL 430 ANGLE products to Western and Eastern Europe, Saudi Arabia, Bangladesh, United States, United Arab Emirates, Canada, Angola, Argentina, Austria, Azerbaijan, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia etc. We are sure that we also can cover the requirements requested by your company you can email us at
harshsteel@ymail.com for your instant requirements.