Stainless steel 15 – 5 PH, also known as UNS S15500 or XM-12, is a modification of 17-4 PH developed in the 60′s. UNS S15500 stainless steel has a more refined microstructure as a result of the remelting process in which it was developed. This refined structure enhances toughness, especially in the transverse direction of the material. UNS S15500 also has excellent corrosion resistance, good fabricating characteristics and low temperature hardening which makes Stainless Steel 15 – 5 PH® the preferred alloy for many industries.
The composition of UNS S15500 includes small amounts of carbon, manganese, phosphorus, columbium (or niobium), tantalum, silicon and sulphur. 15500 can be forged, welded and formed. Machining may be performed in the solution-annealed state or in the final heat treat condition. Desired mechanical properties such as ductility and strength can be achieved through heating the material at various temperatures.
UNS S15500 is a martensitic precipitation hardening grade. Martensitic stainless steels were designed as a type of alloy which is corrosion resistant and could also be hardened through heat treatment.
HEAT TREATED 15-5PH STAINLESS STEEL
Heat treatments are used to strengthen 15-5 alloys. There are eight standard conditions for 15-5 stainless steel after treatment - H 900, H 925, H 1025, H 1075, H 1100, H 1150 and H 1150-M. Heat treating 15-5 PH follows the following steps:
- Conditioning using austenite.
- Air cooling, which turns the austenite into martensitic.
- Precipitation hardening until the desired condition is reached.
Harsh steel provides the following 15-5ph products as below:-
- Conditioning using austenite.
- Air cooling, which turns the austenite into martensitic.
- Precipitation hardening until the desired condition is reached.
Harsh steel provides the following 15-5ph products as below:-
- Sheet and Plate
- AMS 5862
- BMS 7-240
- Bar/Forging
- AMS 5659
- ASTM-A-484
- ASTM-A-564
15-5 PH can be further heat-treated when in precipitation-hardened condition to provide improved resistance to stress corrosion cracking for high temperature applications. Fabrication is recommended after the metal has been heat treated to minimize distortion and stress.
Harsh steel also carries a number of other stainless steel alloys, including347 Stainless, A-286, 321 Stainless, 13-8 MO, AM 350, 17-4 PH Stainless,15-7 MO, 17-7 PH Stainless and 410 Stainless.
Industries that use 15500 include:
- Aerospace
- Chemical
- Food processing
- General metal working
- Paper industries
- Petrochemical
Products partially or completely constructed of 15500 include:
- Aircraft components
- Cylinders
- Engine parts
- Fittings
- Gears
- Hallow shafts
- Marine gas turbine compressor sections
- Paper mill equipment
- Shafts
- Valves
| Material Type | Condition | Ultimate Tensile Strength (PSI) | 0.2% Yield Strength (PSI) | Elongation (% In 2in.) | Reduction Of Area (%) | Hardness Brinell | Hardness Rockwell |
|---|---|---|---|---|---|---|---|
| 15-5 PH | H900 | 190,000 | 170,000 | 6 | 15 | 388 | C40 |
| H1025 | 155,000 | 145,000 | 8 | 27 | 331 | C35 | |
| H1075 | 145,000 | 125,000 | 9 | 28 | 311 | C32 | |
| H1150 | 135,000 | 105,000 | 11 | 30 | 277 | C28 | |
| H1150-M | 115,000 | 75,000 | 14 | 35 | 255 | C24 |
Stainless steel 15 – 5 PH, also known as UNS S15500 or XM-12, is a modification of 17-4 PH developed in the 60′s. UNS S15500 stainless steel has a more refined microstructure as a result of the remelting process in which it was developed. This refined structure enhances toughness, especially in the transverse direction of the material. UNS S15500 also has excellent corrosion resistance, good fabricating characteristics and low temperature hardening which makes Stainless Steel 15 – 5 PH® the preferred alloy for many industries.
The composition of UNS S15500 includes small amounts of carbon, manganese, phosphorus, columbium (or niobium), tantalum, silicon and sulphur. 15500 can be forged, welded and formed. Machining may be performed in the solution-annealed state or in the final heat treat condition. Desired mechanical properties such as ductility and strength can be achieved through heating the material at various temperatures.
UNS S15500 is a martensitic precipitation hardening grade. Martensitic stainless steels were designed as a type of alloy which is corrosion resistant and could also be hardened through heat treatment.
HEAT TREATED 15-5PH STAINLESS STEEL
Heat treatments are used to strengthen 15-5 alloys. There are eight standard conditions for 15-5 stainless steel after treatment - H 900, H 925, H 1025, H 1075, H 1100, H 1150 and H 1150-M. Heat treating 15-5 PH follows the following steps:
- Conditioning using austenite.
- Air cooling, which turns the austenite into martensitic.
- Precipitation hardening until the desired condition is reached.
Harsh steel provides the following 15-5ph products as below:-
- Conditioning using austenite.
- Air cooling, which turns the austenite into martensitic.
- Precipitation hardening until the desired condition is reached.
Harsh steel provides the following 15-5ph products as below:-
- Sheet and Plate
- AMS 5862
- BMS 7-240
- Bar/Forging
- AMS 5659
- ASTM-A-484
- ASTM-A-564
15-5 PH can be further heat-treated when in precipitation-hardened condition to provide improved resistance to stress corrosion cracking for high temperature applications. Fabrication is recommended after the metal has been heat treated to minimize distortion and stress.
Harsh steel also carries a number of other stainless steel alloys, including347 Stainless, A-286, 321 Stainless, 13-8 MO, AM 350, 17-4 PH Stainless,15-7 MO, 17-7 PH Stainless and 410 Stainless.
Industries that use 15500 include:
- Aerospace
- Chemical
- Food processing
- General metal working
- Paper industries
- Petrochemical
Products partially or completely constructed of 15500 include:
- Aircraft components
- Cylinders
- Engine parts
- Fittings
- Gears
- Hallow shafts
- Marine gas turbine compressor sections
- Paper mill equipment
- Shafts
- Valves
| Material Type | Condition | Ultimate Tensile Strength (PSI) | 0.2% Yield Strength (PSI) | Elongation (% In 2in.) | Reduction Of Area (%) | Hardness Brinell | Hardness Rockwell |
|---|---|---|---|---|---|---|---|
| 15-5 PH | H900 | 190,000 | 170,000 | 6 | 15 | 388 | C40 |
| H1025 | 155,000 | 145,000 | 8 | 27 | 331 | C35 | |
| H1075 | 145,000 | 125,000 | 9 | 28 | 311 | C32 | |
| H1150 | 135,000 | 105,000 | 11 | 30 | 277 | C28 | |
| H1150-M | 115,000 | 75,000 | 14 | 35 | 255 | C24 |
HEX BARS PRODUCT OVERVEIW
| Stainless Steel Hex Bar | |
|---|---|
| Thickness Range of Flat Bar | 3/16″ thru 3″ Larger sizes available upon request |
| Grades | 202, 304/304L, 316/316L,304H, 316H, 309/S, 310/S, 317/L, 321/H, 347/H, 904L, 330, 254SMO, 410. In duplex grades, we can supply 2205 and 2507. Some nickel Alloy such as alloy 200/201, C276, Alloy 400, Alloy 600, Alloy 625, Alloy 800H, Alloy 800HT, 254SMO, AL6XN and others Titanium alloys and copper alloys are also available |
INVENTORY:
| Size in Inches | Wt per Ft | Wt per 12′ | 303 | 304/L | 316/L | 416 |
|---|---|---|---|---|---|---|
| 3/16″ | 0.104 | 1.248 | X | X | X | X |
| 1/4″ | 0.180 | 2.160 | X | X | X | X |
| 5/16″ | 0.290 | 3.480 | X | X | X | X |
| 3/8″ | 0.410 | 4.920 | X | X | X | X |
| 7/16″ | 0.560 | 6.72 | X | X | X | X |
| 1/2″ | 0.740 | 8.880 | X | X | X | X |
| 9/16″ | 0.930 | 11.16 | X | X | X | X |
| 5/8″ | 1.150 | 13.80 | X | X | X | X |
| 11/16″ | 1.390 | 16.68 | X | X | X | |
| 3/4″ | 1.660 | 19.92 | X | X | X | X |
| 13/16″ | 1.950 | 23.40 | X | X | X | |
| 7/8″ | 2.300 | 27.60 | X | X | X | X |
| 15/16″ | 2.600 | 31.20 | X | X | X | X |
| 1″ | 2.90 | 34.80 | X | X | X | X |
| 1-1/16″ | 3.30 | 39.60 | X | X | X | X |
| 1-1/8″ | 3.700 | 44.40 | X | X | X | X |
| 1-1/4″ | 4.600 | 55.20 | X | X | X | X |
| 1-5/16″ | 5.100 | 61.20 | X | X | X | |
| 1-3/8″ | 5.600 | 67.20 | X | X | X | X |
| 1-7/16″ | 6.100 | 73.20 | X | X | X | |
| 1-1/2″ | 6.600 | 79.20 | X | X | X | X |
| 1-5/8″ | 7.800 | 93.60 | X | X | X | |
| 1-3/4″ | 9.030 | 108.36 | X | X | X | X |
| 1-7/8″ | 10.400 | 124.80 | X | X | X | X |
| 2″ | 11.80 | 141.60 | X | X | X | X |
| 2-1/4″ | 14.920 | 179.04 | X | X | X | X |
| 2-3/8″ | 16.920 | 203.04 | X | X | X | |
| 2-1/2″ | 18.42 | 221.04 | X | X | X | X |
| 3″ | 26.53 | 318.36 | X | X | X | X |
STAINLESS STEEL BAR VALUE ADDED OPTIONS:
| Stainless Steel Bar Value Added Options | |
|---|---|
| Stainless Steel Bar Polishing | Harsh Steel can polish nearly any stainless steel bar item to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Stainless steel polished bar can also be cut to size. Pitt free surfaces can also be provided. |
| Heatreating & Annealing | Some grades of stainless steel bars can be heatreated to change the mechanical properties. Precipitation Hardening Stainless Steels such as 17-4PH can be heatreated. 410 stainless steel bar can also be heatreated. In some cases, secondary annealing 300 series stainless steel may be required depending on the application |
| Positive Material Identification (PMI) | Harsh Steel can perform PMI testing in house for most stainless steel grades, or we can work with independent labs to complete PMI in order to meet customer specifications. |
| UT Testing | In some cases, UT testing of the stainless steel bar may be required. We can assist you with this requirement. |
- Need 1,100 pieces of 7/8″ 303 round bar cut to 2-1/8″ long? We can process this job in a few days with our Amada CM100CNC with precise part tolerances
- Rapid cut of round bar 5/8″ thru 4″ dia
- Larger stainless bar cutting thru 26″ in diameter
- Multiple cutting stations allow us to ship cut stainless bar to size when you need it.
- Grinding and polishing available upon request
- Special heat treat requirements can also be supplied. Ask for details.
- Stainless round bars can also be polished or center-less ground to exact tolerances.
We export our PRECIPITATION HARDENING STAINLESS STEEL 15-5PH HEX BARS products to Western and Eastern Europe, Saudi Arabia, Bangladesh, United States, United Arab Emirates, Canada, Angola, Argentina, Austria, Azerbaijan, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia etc. We are sure that we also can cover the requirements requested by your company you can email us at harshsteel@ymail.com for your instant requirements.